Product Details:
Ash content | 7% max |
Acetone extract | 16% max |
Carbon black | 27% min |
Mooney Viscosity | 45 - 50 |
Tensile strength | 8 mpa min |
Elongation at break | 260% min |
Volatile matter | 0.1% max |
R H C by diff | 48% min |
Specific gravity | 1.05 - 1.15 |
Product Details:
Minimum Order Quantity | 500 Kilogram |
Material | Latex Rubber |
Specific Gravity | 1.09 +- 0.05 Kg/m3 |
Ash content | 15% max |
Acetone extract | 10%max |
Standard | 7 Mpa - 14Mpa |
Weight | 25kg/PC |
R H C by diff | 80% min |
Packing | Pack by Plastic Film , Woven Bag or Pallet. |
Mooney Viscosity | 30 min ML (1+4) 100 degree C |
Moisture Content | 1% |
Appearance | White Rubber Sheet |
Additional Information:
Product Details:
Application | Automobile Parts |
Specific Gravity | 1.09 +/- 0.05 |
Ash Content | 15% max |
Acetone Extract | 10% max |
Moisture Content | 1% max |
Pcakging Size | 25 kg |
Packaging Type | Bag |
R H C by diff | 80% min |
Mooney Viscosity | 30 min |
Product Details:
Packaging Type | Bag |
Ash content | 7% max |
Carbon black | 27% min |
R H Cby diff | 48% min |
Specific gravity | 1.05 - 1.15 |
Tensile strength | 70 Kgs/cm2 min |
Acetone extract | 16%max |
Volatile matter | 0.1% max |
Application | Automobile Extruded Parts |
Elongation at break | 310% min |
Packaging Size | 50 - 100 kg |
Product Details:
Color | Black |
Specific Gravity | 1.14 +- 0.02% |
Elongation at Break | 485%min |
Mooney viscosity | 30-45 at 100 degree C |
RHC by Diff | 50% min |
Volatile Matter | 0.1% max |
Hardness Shore A | 51 +- 3 |
Ash Content | 4 +- 2% |
Tensile Strength | 48 Kgs/cm 2 min |
Acetone Extract | 9 +- 3% |
Carbon Black | 30 +- 3%max |
Product Details:
Application | Automobile Extruded Parts |
Specific Gravity | 1.1 - 1.2 Kg/m 3 |
Ash Content | 15% max |
Tensile Strength | 65 Kg/cm2 min |
Carbon black | 24% min |
Rubber Hydrocarbon | 30% |
Elongation at break | 450 % min |
Hardness at Shore A | 55 +/- 5 |
Mooney Viscosity | 25 - 45 Cgs |
R H C by diff | 50% min |
Product Details:
Material | Rubber |
Color | Black |
Use | Industrial |
Packaging Size | 50 kg |
Packaging Type | Bag |
Product Details:
Minimum Order Quantity | 100 Kg |
Quantity Per Pack | 20 kg |
Acetone Extraction | 3 - 5% |
Ash Contetnt | 15 % max |
Bulk Density | 0.30 - 0.45 gm |
Sieve Analysis Passing Mesh | 95 % min |
Nbr Content By Diff | 65 % min |
Additional Information:
Product Details:
Hardness | 50 Shore A |
Application | Automotive |
Ash Content | 10.0% |
Color | Black |
Acetone Extract | 22.0 % max |
Heating on Loss | 1.0% |
Elongation at Break | 360.0% min |
Gel Content | 90.0% |
Country of Origin | Made in India |
Product Details:
Minimum Order Quantity | 1000 Kilogram |
Color | Black |
Material | Rubber |
Application | Butyl Inner Tubes, Tyre Inner Liner etc |
Packaging Size | 100 kg |
Packaging Type | Bag |
Butyl Reclaim Rubber can be provided in best quality by us. It is very fine product recycled out of butyl rubber tube scrap. The scrap butyl tubes are pure good quality butyl. Also it is a harder and less porous material than other and has enough elasticity to form an airtight seal.
Price Range: Rs 60 - 65/kg
Product Details:
Minimum Order Quantity | 1 kg |
Color | Black |
Material | Rubber |
Type | Precured Tread Rubber |
Raw Materials | Natural Rubber, Carbon Blacks, Oils, Rubber Chemicals. |
Applications | Tyre Retreading |
Other than the Precured Tread Rubber, we are also manufacturing other Tyre Retreading materials as mentioned below:
Note: Price may be negotiable as per order quantity and may vary irrespective of prior notice.
Additional Information:
Product Details:
Color | Yellowish |
Ash content | 1.0 max |
Mooney Viscosity | 45 +/- 10 ML 1+4 at 100 0 C |
Styrene Content | 40 +/- % |
Density | 0.92 g/cm 2 |
Moisture Content | 0.5 % max |
Packing | 30 kg bales |
Additional Information:
Product Details:
Material | Tyre Scraps |
Weight | 200 MT |
Acetone Extract | 16%max |
Carbon black | 27% min |
Volatile Matter | 0.1% max |
Tensile Strength | 48Kgs/cm2 min |
Elongation at break | 220 min |
Ash Content | 8% max |
RHC by Diff | 47% min |